1000*2000mm Plastic Polyoxymethylene POM Sheet

• Material: POM
• Kind: Hard Plastic Sheet
• Water Absorption: 0.24%
• Model NO.: POM-C Sheet
• Contraction Percentage: ＜0.4%
• Tensile Strength: 66.6 MPa
• Thickness: 5-100mm, Others
• Color: White, Black, Others
• Density: 1.4G/Cm3
• Market: Euro, Asia, Central and South America
• Transport Package: Pallet
• Specification: 1000x2000mm, others
• Trademark: HJH
• Origin: China
• HS Code: 3920999090
• Production Capacity: 200 Tons / Month
• Package Size: 105.00cm * 205.00cm * 80.00cm
• Package Gross Weight: 1000.000kg

Product Description

Re: Polyoxymethylene (POM) Sheet

POM plastic particles are extruded by an extruder at high temperature, and then extruded through the corresponding die mouth to obtain sheets of different thicknesses. It is a kind of thermoplastic engineering plastic with high melting point and high crystallinity. Because of the good characteristics, it is very suitable for machining on automatic lathe, especially for manufacturing precision parts.
 

1. Features:

High mechanical strength, high rigidity, high hardness, excellent elasticity, sliding and abrasion resistance, good creep resistance, even at low temperatures, high impact strength, excellent dimensional stability, excellent mechanical performance, physiological inertia, suitable for contact with food.
 

2. Applications:

POM sheets are widely used to manufacture various sliding rotating machinery, precision parts, gears, bearings, etc. The use industry covers automobile, electronics, clothing, medical, machinery, sports equipment and other fields.
 

3. Types:

POM-C/H (black and white) represents POM copolymer (POM-C) and POM homopolymer (POM-H) respectively. POM copolymer has low melting point, thermal stability, chemical corrosion resistance, flow characteristics, hydrolysis resistance, strong alkali resistance and thermal oxidation degradation, and its processability is better than homoformaldehyde. POM homopolymer has higher crystallinity, creep resistance, lower thermal expansion rate, and wear resistance, mechanical strength, rigidity & thermal deformation temperature better than copolymer formaldehyde. (At present, POM-C is widely used for POM semi-finished products on the market.)
 

4. Test Report:

No.	Item	Unit	Result	Test Method
1	Density	g/cm³	1.413	GB/T 1033.1 -2008
2	Tensile strength	MPa	66.6	GB/T 1040 .2/1B-2006
3	Elongation at break	%	24
4	Bending strength	MPa	102	GB/T 9341 -2008
5	Modulus of elasticity in static bending	MPa	2820
6	Charpy Notched Impact Strength	kJ/m²	7.8	GB/T 1043 . 1/1eA -2008
7	Impact intensity of falling ball	/	No cracking	GB/T 13520 - 1992
8	Vicat heat resistance (1kg ,50C/h)	ºC	163	GB/T 1633 -2000
9	Variation Rate Of Heating Sizes(longitudinal)	%	0.08	GB/T 22789.1 -2008
10	Variation Rate Of Heating Sizes(transverse)	%	0.04
11	Rockwell hardness	/	118	GB/T 3398.2 -2008
12	Surface resistance coefficient	Ω	8.5×1012	GB/T 1410 -2006
13	Volume resistance coefficient	Ω · m	1.3×1012
14	Dielectric constant (1MHz)	/	3.7	GB/T 1409 -2006
15	Dielectric loss	/	0.055
16	Dielectric strength	kV/mm	6.93	GB/T 1408.1 -2016
17	Friction coefficient	/	0.18	GB/T 3960 -2016

 

5. Specifications:

*Length x Width: 1000x2000mm, others
*Thickness: 5~100mm, others

6. Package:
Sheets packed in pallet.

7. Product Photos:


FAQ
Q: Are you trading company or manufacturer ?
A: Both

Q: How long is your delivery time?
A: Generally it is 3-5 days if the goods are in stock. or it is 5--15days if the goods are not in stock, it is according to quantity.

Q: Do you provide samples ?is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.

Q: What is your terms of payment ? A: Payment<=2000USD, 100% in advance. Payment>=2000USD, 30% T/T in advance ,balance before shipment.